BLOOM(SUZHOU) MATERIALS CO.,LTD
Attitude Is Everything.Details Determine Success or Failure.
 |
| Brand Name: | BLM-ML-1 |
| Minimum Order Quantity: | Negotiation |
|---|---|
| Price: | Negotiation |
| Packaging Details: | packed and labeled according to the regulations and customer's requests.Great care is taken to avoid any damage which might otherwise be caused during storage or transportation. |
| Delivery Time: | 25-30 days subject to the clients' requirement and quantity |
| Payment Terms: | Western Union, L/C, T/T |
| Supply Ability: | 300 Ton/Tons per Month |
| Place Of Origin: | Jiangsu, China (Mainland) | Standard: | AISI, ASTM, BS, DIN, GB, JIS, Other,JIS,AISI,ASTM,GB,DIN,EN |
|---|---|---|---|
| Grade: | Monel Nickel Alloy | Technique: | Hot Rolled |
| Surface Treatment: | Bright Or Black | Application: | Electrical Industry |
| Delivery: | 25-30 Days After The Payment | Price Term: | Ex-Work,FOB,CNF,CFR,CIF,FCA,DDP,DDU |
| High Light: | monel 400 material,monel k500 sheet |
||
Monel 500 sheet
Monel K500 material is a nickel-copper alloy that combines the excellent corrosion resistance characteristic of Monel 400 with the added advantage of greater strength and hardness. These amplified properties, strength and hardness, are obtained by adding aluminum and titanium to the nickel-copper base and by a thermal processing used to effect precipitation, typically called age hardening or aging. When in the age-hardened condition, Monel K-500 has a greater tendency toward stress-corrosion cracking in some environments than Monel 400. Alloy K-500 has approximately three times the yield strength and double the tensile strength when compared with alloy 400. Plus, it can be further strengthened by cold working prior to precipitation hardening. The strength of this nickel steel alloy is maintained to 1200° F but stays ductile and tough down to temperatures of 400° F. Its melting range is 2400-2460° F.
Specification
| UNS | W.Nr |
| N05500 | 2.4375 |
Chemical composition
| Grade | % | Ni | Cu | Al | Ti | Fe | Mn | S | C | Si |
| K500 | Min | 63 | 27.0 | 2.30 | 0.35 | |||||
| Max | 33.0 | 3.15 | 0.85 | 2.0 | 1.5 | 0.01 | 0.25 | 0.5 |
Mechanical properties:(Minimum value at 20°C)
|
Tensile Strength σb/MPa |
Yield Strength σp0.2/MPa |
Elongation σ5 /% |
| 1100 | 790 | 20 |
Specification
| UNS | W.Nr |
| N05500 | 2.4375 |
Chemical composition
| Grade | % | Ni | Cu | Al | Ti | Fe | Mn | S | C | Si |
| K500 | Min | 63 | 27.0 | 2.30 | 0.35 | |||||
| Max | 33.0 | 3.15 | 0.85 | 2.0 | 1.5 | 0.01 | 0.25 | 0.5 |
Mechanical properties:(Minimum value at 20°C)
|
Tensile Strength σb/MPa |
Yield Strength σp0.2/MPa |
Elongation σ5 /% |
| 1100 | 790 | 20 |
Specification
| UNS | W.Nr |
| N05500 | 2.4375 |
Chemical composition
| Grade | % | Ni | Cu | Al | Ti | Fe | Mn | S | C | Si |
| K500 | Min | 63 | 27.0 | 2.30 | 0.35 | |||||
| Max | 33.0 | 3.15 | 0.85 | 2.0 | 1.5 | 0.01 | 0.25 | 0.5 |
Mechanical properties:(Minimum value at 20°C)
|
Tensile Strength σb/MPa |
Yield Strength σp0.2/MPa |
Elongation σ5 /% |
| 1100 | 790 | 20 |
Monel K500 Applications
Contact Person: Kara Liu
Tel: 0086-13914912658
Polished Duplex 2205 Round Bar , S31803 Stainless Steel Round Bar High Alloy Steels
Alloy Duplex 2507 Plate With Superior Chloride Pitting Resistance
S32900 Duplex Stainless Steel Bar / Rod For Desalination Equipment
S32760 Stainless Steel Metal Strips With Erosion Corrosion Resistance
15-5 PH Bar Precipitation Hardening Stainless Steel UNS S15500 Grade For Nuclear Waste Casks
High Toughness 17 4 Steel Plate , 17 4ph Plate For Shaft And Bearing
Low Carbon Content 17 7PH Plate With Superior Weldability 0.282 Lb / Inch3 Density
Stainless Steel Inconel 625 Bar With Stress Corrosion Cracking Resistance
8mm-100mm Thickness Inconel Nickel Alloy Plate , Inconel 718 Plate Mill Edge
Special Metals Inconel 718 Bar , Nickel Alloy 718 With Ending Machinability
Wonderful Machining And Welding Inconel 625 Material Nickel Plate Type