Uns N05500 Monel Nickel Alloy 500 Wire With Outstanding Corrosion Resistance

Product Details:

Place of Origin:	Jiangsu, China (Mainland)
Brand Name:	BLM-ML-1

Payment & Shipping Terms:

Minimum Order Quantity:	Negotiation
Price:	Negotiation
Packaging Details:	packed and labeled according to the regulations and customer's requests.Great care is taken to avoid any damage which might otherwise be caused during storage or transportation.
Delivery Time:	25-30 days subject to the clients' requirement and quantity
Payment Terms:	Western Union, L/C, T/T
Supply Ability:	300 Ton/Tons per Month

Contact Now

Detailed Product Description

Standard:	AISI, ASTM, BS, DIN, GB, JIS, Other,JIS,AISI,ASTM,GB,DIN,EN	Grade:	Monel Nickel Alloy
Place Of Origin:	Jiangsu, China (Mainland)	Technique:	Hot Rolled
Surface Treatment:	Bright Or Black	Application:	Electrical Industry
Delivery:	25-30 Days After The Payment	Price Term:	Ex-Work,FOB,CNF,CFR,CIF,FCA,DDP,DDU
High Light:	n05500 nickel alloy , monel k500 sheet

Monel 500 WIRE

Descripition:

MONEL®alloy K-500 (UNS N05500/ W.Nr. 2.4375) is a nickel-copper alloy which combines the excellent
corrosion resistance of MONEL alloy 400 with the added advantages of greater strength and hardness.

The increased properties are obtained by adding aluminum and titanium to the nickel-copper base,

and by heating under controlled conditions so that submicroscopic particles of Ni 3 (Ti, Al) are precipitated

throughout the matrix. The thermal processing used to effect precipitation is commonly called age hardening or aging. The composition of the alloy is given in Table 1. Typical applications for MONEL alloy K-500
products are chains and cables, fasteners and springs for marine service; pump and valve components for
chemical processing; doctor blades and scrapers for pulp processing in paper production; oil well drill
collars and instruments, pump shafts and impellers, non-magnetic housings, ety lifts and valves for oil
and gas production; and sensors and other electronic components.

Monel K-500 Chemical composition:

Alloy	%	Ni	Cu	Al	Ti	Fe	Mn	S	C	Si
Monle K500	Min.	63	27.0	2.30	0.35
Monle K500	Max.		33.0	3.15	0.85	2.0	1.5	0.01	0.25	0.5

Monel K-500 Physical properties:

Density	8.44 g/cm3
Melting point	1315-1350°C

Monel K-500 minimum mechanical properties in the room temperature:

Forms	Condition	Max. section Thickness,in.(mm)	Tensile strength Min. Ksi.(Mpa)	Yield strength Min.Ksi.(Mpa)	Elongation in 2 in,or 4D,min.,%	Hardness
Forms	Condition	Max. section Thickness,in.(mm)	Tensile strength Min. Ksi.(Mpa)	Yield strength Min.Ksi.(Mpa)	Elongation in 2 in,or 4D,min.,%	HB min.	HRC min.
Round bars, Hexagons, squares, rectangles and forgings	hot-worked and age hardened	All Sizes	140(965)	100(690)	20	265	27
Round bars	cold worked and age hardened	1/4(6.4)to 1(25.4)	145(1000)	110(760)	15	300	32
		over 1(25.4)to 3(76.2)	140(965)	100(690)	17	280	29
		over 3(76.2)to 4(101.6)	135(930)	99(655)	20	255	25
Hexagons	cold worked and age hardened	1/4(6.4)to 2(50.8)	140(965)	100(690)	15	265	27
Round bars, Hexagons, squares, rectangles and forgings	Annealed and age hardened	Up to 1(25.4)	130(895)	90(620)	20	250	24
Round bars, Hexagons, squares, rectangles and forgings	Annealed and age hardened	1(25.4)and over	130(895)	85(585)	20	250	24has approximately twice the tensile strength and triple the yield strength of Alloy 400. The strength of Alloy K-500 is maintained to 1200 degrees Fahrenheit, but stays ductile and tough down to temperatures of -400 degrees Fahrenheit. Alloy K-500 also stays non-magnetic to -200 degrees Fahrenheit.

Additional characteristics of Alloy K-500 include outstanding corrosion resistance in a wide range of chemical and marine surroundings, from salts and alkalis, non-oxidizing acids to pure water. Alloy K-500 is non-magnetic and spark resistant. It is also recommended that Alloy K-500 be annealed when it is welded and that any weldments be stress relieved prior to aging.

Industries Served:

Uns N05500 Monel Nickel Alloy 500 Wire With Outstanding Corrosion Resistance 0