|Place of Origin:||Jiangsu, China (Mainland)|
|Minimum Order Quantity:||Negotiation|
|Packaging Details:||packed and labeled according to the regulations and customer's requests.Great care is taken to avoid any damage which might otherwise be caused during storage or transportation.|
|Delivery Time:||25-30 days subject to the clients' requirement and quantity|
|Payment Terms:||Western Union, L/C, T/T|
|Supply Ability:||300 Ton/Tons per Month|
|Standard:||AISI, ASTM, BS, DIN, GB, JIS, Other,JIS,AISI,ASTM,GB,DIN,EN||Grade:||FeNi36|
|Thickness:||8mm-100mm||Place Of Origin:||Jiangsu, China (Mainland)|
|Surface Treatment:||Black Surface||Application:||As Raw Material Produce OLED Frame,machine,high Temperature,oil,gas,oil Well,corrosive Environments|
|Special Use:||Invar36,4j36||Delivery:||25-30 Days Subject To The Clients' Requirements And Quantity|
invar 36 wire,
invar 36 plate
Hot Rolled And Forged Plate Black Surface Invar36 1710 x 1110 x 31mm,OLED Frame
1 . Descriptions:
Invar, also known as Nickel Alloy 36, is a nickel-iron alloy noted for its uniquely low coefficient of thermal expansion. The name Invar comes from the word invariable, due to its relative lack of expansion or contraction with temperature changes. Invar was invented in 1896 by Swiss scientist Charles Édouard Guillaume, who received the Nobel Prize in Physics in 1920 for the discovery, which enabled improvements in scientific instruments.
Invar is an austenitic alloy. It is strong, tough, ductile and possesses a useful degree of corrosion resistance. It is magnetic at temperatures below its Curie point and non-magnetic at temperatures above. Invar is therefore always magnetic in the temperature range in which it exhibits the low expansion characteristics. Invar is the standard alloy for low expansivity up to 400 oF. For applications at higher temperatures, the higher nickel alloys are recommended.
2 . Specification:
|Grade||Tensile Strength Rm N/mm²||Yield Strength Rp0.2 N/mm²||Elongation A5 ％||Hardness|
6 . Features:
36 alloy is a special ultra-low coefficient of heat expansion of low-iron-nickel alloy. One of carbon and manganese element of control is very important. Cold deformation can reduce the coefficient of thermal expansion, in particular within the framework of the heat treatment temperature coefficient of thermal expansion will enable stabilization. Has the following characteristics: 1.Has very low coefficient of heat expansion between the temperature of -250ºC and 200ºC. 2.Good toughness and plastic Metallurgical structure Invar 36 is the face centered cubic lattice structure Corrosion resistance Invar 36 has corrosion resistance in the dry air of room temperature.In other harsh environments, such as the humid air, there may be corrosion (rust).